| PC transparent glossy sheet | |||||||
|---|---|---|---|---|---|---|---|
| product name | Thickness (mm) | Width (mm) | Length (mm) | The number per stake | net weight | ||
| Slice * package | The total amount | Kg / piece | Kg / care | ||||
| JR1-1 polishing / polishing | 0.30 | 915 | 1830 | 25-40 | 1000 | 0.60 | 600 |
| 0.50 | 915 | 1830 | 30 * 20 | 600 | 1.00 | 600 | |
| 0.70 | 915 | 1830 | 20 * 20 | 400 | 1.40 | 560 | |
| 1220 | 2440 | 2.50 | 1000 | ||||
| 0.80 | 915 | 1830 | 25 * 15 | 378 | 1.60 | 600 | |
| 1220 | 2440 | 2.86 | 1072 | ||||
| 1.00 | 915 | 1830 | 30 * 10 | 300 | 2.00 | 600 | |
| 1220 | 2440 | 3.57 | 1071 | ||||
| PC transparent glossy web | ||||
|---|---|---|---|---|
| product name | Thickness (mm) | Each volume size | net weight | |
| Width (mm) | Length (m) | Kg / lb | ||
| JR1-1 polishing / polishing | 0.100 | 927 | 400 | 44.5 |
| 0.125 | 927 | 400 | 55.6 | |
| 0.175 | 927 | 350 | 68.1 | |
| 0.250 | 927 | 300 | 83.4 | |
| 0.300 | 927 | 250 | 83.4 | |
| 0.375 | 927 | 200 | 83.4 | |
| 0.500 | 927 | 150 | 83.4 | |
| 1220 | 109.8 | |||
| 0.76 | 927 | 100 | 84.5 | |
| 1220 | 111.3 | |||
| PC Scrubbing Coil | ||||
|---|---|---|---|---|
| product name | Thickness (mm) | Each volume size | net weight | |
| Width (mm) | Length (m) | Kg / lb | ||
| JR4-2 sand / matte JR2-1 matte / polished JR4-1 sand / polished JR3-2 fine sand / matte JR3-7 rain silk | 0.075 | 930 | 1000 | 83.7 |
| 0.125 | 930 | 640 | 89.3 | |
| 0.175 | 930 | 457.2 | 89.3 | |
| 0.25 | 930 | 327.6 | 91.4 | |
| 0.375 | 930 | 228.6 | 95.7 | |
| 0.500 | 930 | 175.3 | 978 | |
| 0.760 | 930 | 114.3 | 96.9 | |
| PC film sheet product characteristics | ||||
|---|---|---|---|---|
| Serial number | Physical properties | Performance | unit | standard test |
| Physical performance | density | 1.32 | G / cm3 | ISO 1183 |
| Haze | 92 | % | ASTM D1003 | |
| Transmittance | 85 | % | ASTM D1003 | |
| Mechanical behavior | Tensile Strength | 65 | MPa | ISO 527 |
| Elongation at break | > 100 | % | ISO 527 | |
| Tensile modulus | 2200 | MPa | ISO 527 | |
| Bending strength | 91 | MPa | ISO 178 | |
| Surface Tension | > 38 | Dyn / cm | Test solution | |
| Surface hardness | 2B ~ B | - | Test pen | |
| Electrical performance | Dielectric constant | 3 | - | IEC 60250 |
| Endurance pressure | 59 | KV / mm | IEC 60243 | |
| Arc resistance | 250 | - | IEC 60112 | |
| Surface resistivity | 1.00E + 16 | Ω / square | IEC 60093 | |
| Volume resistivity | 1.00E + 17 | Ω-cm | IEC 60093 | |
| CTI | 3 | - | UL94 | |
| Thermal performance | Thermal expansion coefficient | 5.8 | X 10-5 / ° C | ISO 11359 |
| Thermal conductivity | 0.2 | W / (m * K) | ASTM D5470 | |
| Shrinkage (150 ° C) | 0.5 to 0.7 | % | ASTM D1204 | |
| Glass transition temperature | 153 | ℃ | ISO 11357 | |
| Vicat softening point | 156 | ℃ | ISO 11357 | |
| Flammability | Flammability rating | V-0 / VTM-0 | E249605 | |
| Note: This test is for reference only, not as an absolute application of indicators | ||||